增塑剂 KW-15 产品规格说明书
2)良好的低温表现 3)与PVC良好的兼容性 4)良好的加工性能(优秀的塑化融合性能)。 |
产 地:日本
技术参数 50phr(A) 80phr(B)
No. |
1 |
2 |
3 |
Plasticizer Viscosity25℃(mPa.s) |
KW-15 |
KW-13 |
KW-10 |
3050 |
2930 |
2870 |
Hardness;Shore A,at23℃
A |
AfterOsec/aftr5sec |
92/88 |
92/89 |
94/90 |
B |
afterOsec/after5sec |
73/68 |
73/69 |
74/68 |
Low Temperature Property
A |
Clash berg(℃) |
-9 |
-10 |
-6 |
Brittle Point(℃) |
-15 |
-16 |
-11 |
|
B |
Clash berg(℃) |
-26 |
-28 |
-24 |
Brittle Point(℃) |
-30 |
-32 |
-26 |
Tensile Properties at 23℃,thickness 1mm
A |
100%Modulus(MPa) |
12.8 |
12.4 |
14.2 |
Tensile Strength(MPa) |
21.3 |
21.1 |
21.9 |
|
Elongation(%) |
324 |
325 |
326 |
Heat Aging136×168hrs,thickness 1mm,():retention
A |
100%Modulus(MPa) |
13.7(107) |
13.7(111) |
15.3(108) |
Tensile Strength(MPa) |
20.9(98) |
21.2(101) |
21.9(100) |
|
Elongation(%) |
314(97) |
315(97) |
319(98) |
|
Weight Loss(%) |
2.2 |
2.2 |
2.2 |
Oil Aging(JIC No.2Insulation oil)100℃×120hrs,thickness 1mm,():retention
A |
100%Modulus(MPa) |
17.9(140) |
17.3(139) |
19.9(140) |
Tensile Strength(MPa) |
22.4(105) |
22.5(107) |
22.6(103) |
|
Elongation(%) |
279(86) |
293(90) |
261(80) |
|
Weight Loss(%) |
2.4 |
1.2 |
2.6 |
Non-migration Property:ABS(Stylacl21)X ℃×72hrs,load;0.22Kg/cm2
A |
60℃ |
○ |
○ |
○ |
70℃ |
○ |
○ |
○ |
|
B |
60℃ |
○ |
○ |
○ |
70℃ |
○ |
△ |
○ |
Non-migration Property:HIPS(HGI-02)X ℃×72hrs,load;0.22Kg/cm2
A |
60℃ |
○ |
○ |
○ |
70℃ |
○ |
○ |
○ |
|
B |
60℃ |
○ |
○ |
○ |
70℃ |
○ |
○ |
○ |
【Formulation】 【Processing】 A B
PVC(P=1000)100 Roll 170℃×7min 155℃×7min
Plasticizer 50 or 80 Press 170℃×5min 170℃×5min
MP-677E 4